COREA METAL SERVICE
COMES PRODUCTS
TUBE
SYMBOL | GRADE | CHEMICAL | MECHANICAL PROPERTIES | |||||||
---|---|---|---|---|---|---|---|---|---|---|
C | SI | Mn | P | S | Tensile Strength [Mpa] |
Yield Point [Mpa] |
Elongation in 2in or 50㎜(%) |
|||
ASTM (ASME) (S)A179 |
- | 0.06 ~0.18 |
- | 0.27 ~0.63 |
0.035 max. |
0.035 max. |
325min | 180min | 35min | |
ASTM (ASME) (S)A192 |
- | 0.06 ~0.18 |
0.25 max. |
0.27 ~0.63 |
0.035 max. |
0.035 max. |
325min | 180min | 35min | |
ASTM (ASME) (S)A192 |
A-1 | 0.27 max. |
0.10 min |
0.93 max. |
0.035 max. |
0.035 max. |
415min | 255min | 30min | |
C | 0.35 max. |
0.10 max. |
0.29 ~1.06 |
0.035 max. |
0.035 max. |
485min | 275min | 30min | ||
Longitudinal | Transverse | |||||||||
ASTM (ASME) (S)A106 |
A | 0.25 max. |
0.10 min |
0.27 ~0.93 |
0.035 max. |
0.035 max. |
330min | 205min | 35min | 25min |
B | 0.30 max. |
0.10 min |
0.29 ~1.06 |
0.035 max. |
0.035 max. |
415min | 240min | 30min | 16.5min | |
C | 0.35 max. |
0.10 min |
0.29 ~1.06 |
0.035 max. |
0.035 max. |
485min | 275min | 30min | 16.5min |
SYMBOL | GRADE | CHEMICAL | MECHANICAL PROPERTIES | ||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
C | SI | Mn | P | S | Cr | Mo&(v) | Tensile Strength [Mpa] |
Yield Point [Mpa] |
Elongation in 2in or 50㎜(%) |
||
ASTM (ASME) (S)A213 |
T2 | 0.10 ~0.20 |
0.10 ~0.30 |
0.30 ~0.61 |
0.025 max. |
0.025 max. |
0.50 ~0.81 |
0.44 ~0.65 |
415min | 205min | 30min |
T5 | 0.15 max. |
0.50 max. |
0.30 ~0.60 |
0.025 max. |
0.025 max. |
4.00 ~6.00 |
0.45 ~0.65 |
415min | 205min | 30min | |
T5 b | 0.15 max. |
1.00 ~2.00 |
0.30 ~0.60 |
0.025 max. |
0.025 max. |
4.00 ~6.00 |
0.45 ~0.65 |
415min | 205min | 30min | |
T5 c | 0.12 max. |
0.50 max. |
0.30 ~0.60 |
0.025 max. |
0.025 max. |
4.00 ~6.00 |
0.45 ~0.65 |
415min | 205min | 30min | |
T9 | 0.15 max. |
0.25 ~1.00 |
0.30 ~0.60 |
0.025 max. |
0.025 max. |
8.00 ~10.00 |
0.90 ~1.10 |
415min | 205min | 30min | |
T11 | 0.05 ~0.15 |
0.50 ~1.00 |
0.30 ~0.60 |
0.025 max. |
0.025 max. |
1.00 ~1.50 |
0.44 ~0.65 |
415min | 220min | 30min | |
T12A | 0.05 ~0.15 |
0.50 max. |
0.30 ~0.61 |
0.025 max. |
0.025 max. |
0.80 ~1.25 |
0.44 ~0.65 |
415min | 220min | 30min | |
T17 | 0.15 ~0.25 |
0.15 ~0.35 |
0.30 ~0.61 |
0.025 max. |
0.025 max. |
0.80 ~1.25 |
(V:0.15 min) |
415min | 205min | 30min | |
T21 | 0.05 ~0.15 |
0.50 max. |
0.30 ~0.60 |
0.025 max. |
0.025 max. |
2.65 ~3.35 |
0.80 ~1.06 |
415min | 205min | 30min | |
T22 | 0.05 ~0.15 |
0.50 max. |
0.30 ~0.60 |
0.025 max. |
0.025 max. |
1.90 ~2.60 |
0.87 ~1.13 |
415min | 205min | 30min |
SYMBOL | GRADE | CHEMICAL | MECHANICAL PROPERTIES | |||||||
---|---|---|---|---|---|---|---|---|---|---|
C | SI&(Cu) | Mn | P | S | Ni | Tensile Strength [Mpa] |
Yield Point [Mpa] |
Elongation in 2in or 50㎜(%) |
||
ASTM (ASME) (S)A334 |
1 | 0.30 max. |
- | 0.40 ~1.06 |
0.025 max. |
0.025 max. |
- | 380min | 205min | 35min |
3 | 0.19 max. |
0.18 ~0.37 |
0.31 ~0.64 |
0.025 max. |
0.025 max. |
3.18 ~3.82 |
450min | 204min | 30min | |
6 | 0.30 max. |
0.10 min |
0.29 ~1.06 |
0.025 max. |
0.025 max. |
- | 415min | 240min | 30min | |
7 | 0.19 max. |
0.13 ~0.32 |
0.90 max. |
0.025 max. |
0.025 max. |
2.03 ~2.57 |
450min | 240min | 30min | |
8 | 0.13 max. |
0.13 ~0.32 |
0.90 max. |
0.025 max. |
0.025 max. |
8.40 ~9.60 |
690min | 520min | 22min | |
9 | 0.20 max. |
(Cu:0.75 ~1.25) |
0.40 ~1.06 |
0.025 max. |
0.025 max. |
1.60 ~2.24 |
435min | 315min | 28min |
SYMBOL | GRADE | CHEMICAL | MECHANICAL PROPERTIES | ||||||
---|---|---|---|---|---|---|---|---|---|
C | SI | Mn | P | S | Tensile Strength [Mpa] |
Yield Point [Mpa] |
Elongation in 2in or 50㎜(%) |
||
ASTM (ASME) (S)A178 |
A | 0.06 ~0.18 |
- | 0.27 ~0.63 |
0.035 max. |
0.035 max. |
325min | 180min | 35min |
B | 0.35 max. |
- | 0.80 max. |
0.035 max. |
0.035 max. |
415min | 255min | 30min | |
D | 0.27 max. |
0.10 min |
1.0 ~1.50 |
0.030 max. |
0.015 max. |
485min | 275min | 30min | |
ASTM (ASME) (S)A214 |
- | 0.18 max. |
- | 0.27 ~0.63 |
0.035 max. |
0.035 max. |
Hardness Requirements : 72 HRB max. |